Stanyl? TW200B6
聚酰胺 46
產(chǎn)品說明:
30% Carbon Reinforced, Heat Stabilized, Lubricated
Special Features:
Used In:
Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
用途 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.28 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 0.90 | -- | % |
|
流量 | 0.20 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 9.5 | -- | % |
|
平衡, 73°F, 50% RH | 2.6 | -- | % |
|
拉伸模量 |
|
|
| ISO 527-2 |
-- | 3.48E+6 | -- | psi |
|
248°F | 1.45E+6 | -- | psi |
|
320°F | 1.28E+6 | -- | psi |
|
356°F | 1.20E+6 | -- | psi |
|
拉伸應(yīng)力 |
|
|
| ISO 527-2 |
斷裂 | 34800 | 21800 | psi |
|
斷裂, 248°F | 18100 | -- | psi |
|
斷裂, 320°F | 15200 | -- | psi |
|
斷裂, 356°F | 13800 | -- | psi |
|
拉伸應(yīng)變 |
|
|
| ISO 527-2 |
斷裂 | 2.0 | 4.0 | % |
|
斷裂, 248°F | 3.0 | -- | % |
|
斷裂, 320°F | 3.0 | -- | % |
|
斷裂, 356°F | 3.0 | -- | % |
|
彎曲模量 | 2.68E+6 | 1.33E+6 | psi | ISO 178 |
簡支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 3.1 | 3.1 | ft·lb/in2 |
|
73°F | 3.8 | 6.7 | ft·lb/in2 |
|
簡支梁無缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eU |
-22°F | 24 | 24 | ft·lb/in2 |
|
73°F | 29 | 36 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
|
| ISO 180/1A |
-40°F | 3.1 | 3.1 | ft·lb/in2 |
|
73°F | 3.8 | 6.7 | ft·lb/in2 |
|
干燥溫度 | 176 | °F |
干燥時(shí)間 | 4.0 到 8.0 | hr |
料筒后部溫度 | 536 到 608 | °F |
料筒中部溫度 | 572 到 608 | °F |
料筒前部溫度 | 572 到 608 | °F |
射嘴溫度 | 572 到 608 | °F |
加工（熔體）溫度 | 581 到 608 | °F |
模具溫度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背壓 | 290 到 1450 | psi |
螺桿壓縮比 | 2.5:1.0 |
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！