Radilon? A RV500RW 182 NAT 5346
聚酰胺66
PA66 50% glass fiber reinforced injection moulding grade. Heat stabilized. Natural colour.
Suitable for technical parts requiring very high stiffness and high mechanical resistance. Excellent heat ageing properties retention, improved welding lines strength. Especially fit for demanding metal replacement applications.
填料/增強材料 | |
添加劑 | |
特性 | |
用途 | |
RoHS 合規(guī)性 | |
外觀 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.58 | -- | g/cm3 | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 4.0 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
拉伸模量 | 2.54E+6 | -- | psi | ISO 527-2/1A/1 |
拉伸應力 (斷裂) | 35500 | -- | psi | ISO 527-2/1A/5 |
拉伸應變 (斷裂) | 2.9 | -- | % | ISO 527-2/1A/5 |
彎曲模量 2 | 2.32E+6 | -- | psi | ISO 178 |
彎曲應力 2 | 290 | -- | psi | ISO 178 |
簡支梁無缺口沖擊強度 |
|
|
| ISO 179/1eU |
-22°F | 45 | -- | ft·lb/in2 |
|
73°F | 180 | -- | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 419 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 491 | -- | °F | ISO 75-2/Af |
維卡軟化溫度 | 491 | -- | °F | ISO 306/B50 |
熔融溫度 3 | 500 | -- | °F | ISO 11357-3 |
表面電阻率 4 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
體積電阻率 4 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
UL 阻燃等級 (0.031 in) | HB | -- |
| UL 94 |
可燃性 | 0 | -- | in/min | FMVSS 302 |
干燥溫度 - 熱風干燥機 | 176 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 到 4.0 | hr |
|
Dew Point - 熱風干燥機 | -4 | °F |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 536 到 572 | °F |
|
模具溫度 | 176 到 212 | °F |
|
注射速度 | 快速 |
|
|